Note that the composition does not tell the whole story, far from it. Since this is from different source, which don't all agree, som values are probably rounded and/or truncated, but I don't know which ones. A dash usually mean 0, empty entries sometimes do but not always.
C Cr Mn Si Mo V
1.4034 0.4-0.5 12-14.5 1.0 1.0 - - Ni:0.3 DIN:X40 Cr13
1.4109 0.55-0.60 13.5-15 1 1 0.5-0.6 -
1.4110 0.55-0.75 16-18 1.0 1.0 0.55-0.75 - DIN:X55 CrMo14 ~440A
1.4111 1.1 15 1.0 1.0 0.5 0.12 DIN:X110 CrMoV15
1.4112 0.75-0.95 16-18 1.0 1.0 0.75-1.0 0.1 DIN:X90 CrMoV18 ~440B
1.4116 0.45 15 1.0 1.0 0.50 - DIN:X45 CrMoV15
1.4125 0.95-1.2 16-18 1.0 1.0 0.6-0.75 - DIN:X105 CrMo17 ~440C
1.2379 1.55 12 0.3 0.25 0.7 1.0 DIN:X155 CrMo12 1 ~D2
1.2842 0.9 0.35 2.0 0.25 - 0.1 DIN:90 MnV8 ~O1
C Cr Mn Si Mo V
420 0.4-0.5 12-14 - - -
420 M 0.3-0.5 12-14 1.0
425 M 0.40-0.54 13.5-15 0.5 0.8 0.6-1 0.1
T 425 M 0.65 13.5 0.35 1.0
440A 0.6-0.75 16.0-18.0 1.0 1.0 0.75
440B 0.75-0.95 16.0-18.0 1.0 1.0 0.75
440C 0.95-1.2 16.0-18.0 1.0 1.0 0.75
GIN-1 / G-2 0.9 15.5 0.6 0.37 0.3 P:0.02 S:0.03
154 CM 1.05 14.0 0.5 0.3 4
ATS 34 1.0-1.05 13.6-14 0.4 0.15-0.35 3.5-4 P:0.03 S:0.02
ATS 55 1.0 14.0 0.5 0.4 0.6 Co: 0.4 Cu: 0.2
440XH 1.6 16 0.5 0.4 0.8 0.45 Ni:0.35
C Cr Mn Si Mo V
INOX 0.52 15 0.45 0.6 0.5 Victorinox's SAKs, RC 56
Sandvik 120C 0.58 14 0.35 0.35 -
O-1 0.85-1 0.4-0.6 1-1.14 - - 0.3 W:0.4-0.6
W-1 1.0 - 0.35 0.35 -
W-2 0.85-1.5 0.15 0.1-0.4 0.1-0.4 0.1 0.15-0.35 W:0.15 V:
A-2 1.0 5.0 - - 1.0
D-2 1.4-1.6 11.0-13.0 - 0.6 0.7-1.2 1.1 Ni:0.3 W:0.4-0.6
M-2 0.85 4.2 0.25 5 W:6.35
1770 0.7 - 0.5 0.3 Uddeholm 1770
1095 0.9-1.03 - 0.3-0.5 - - - P:0.04 S:0.05
5160 0.56-0.64 0.7-0.9 0.75-1 0.15-0.3 - - P:0.035 S:0.04
52100 1.1 1.5 0.35 0.35 - -
12C27 0.58-0.6 13.5-14 0.35-0.4 0.4 - Sandvik 12C27
13C26 0.65 13.0 0.65 0.4 -
19C27 0.95 13.5 0.65 0.4 -
AUS 6 0.6 14.0 1.0 1.0 - 0.1-0.25 Ni: 0.49 6-A
AUS 8 0.75 14.0 - - 0.2 0.1-0.25 Ni: 0.49 8-A
AUS 10 1.0 14.5 0.5 1.0 0.2 0.1-0.25
BG 42 1.15 14.5 0.5 0.3 4.0 1.2
VG 10 1.00 15.00 0.50 0.60 1.05 0.20 P:0.030
C Cr Mn Si Mo V
CPM-S30V 1.45 14.0 2.0 4.0
CPM-S60V 2.15 17.5 0.4 0-0.5 0.4 5.75 CPM-440V
CPM-S90V 2.2 13 0.4 - 1.0 9 CPM-420V
UHB Elmax 1.7 17.0 0.3 0.4 1.0 3.0
RWL 34 1.05 14.0 0.5 0.5 4.0 0.2
PMC 27 0.6 13.5 0.5 0.5 - -
X-15-T.N. 0.4 15.5 - - 2 0.3 N:0.2
ZDP-189 3.0 20.0
KAD181 2.2 18 - - 2 1
N690 <0.04 28-31 <0.5 <0.5 Ni: 57-63 Cu: <0.5 S: <0.015 Fe: 7-11
C Cr Mn Si Mo V
Stellite 6K 1.9 32.0 2.0 - 1.5 - W:4.5,Ni:3.0, Co:64.0 (so it's not steel)
Talonite 6BH 0.9-1.4 28-32 2.0 - 1.5 - W:4.5,Ni:3, Co:64.0 (so it's not steel)